The final properties of thermosets are strongly dependent on their curing process. Therefore, closely monitoring this process is necessary to assure the manufacturing quality and productivity. In this way, the aim of this study is to develop a simple dielectric module for monitoring and optimizing the industrial curing cycle of thermosets. The module is based on a data acquisition system and an interdigital sensor that remains in contact with the resin throughout the entire curing process. Dielectric analysis (DEA) was performed in a commercial epoxy resin formulation widely used as a matrix for thermoset composites, which was submitted to a pre-established and validated curing cycle. The properties derived from DEA measurements are in accordance with differential scanning calorimetry (DSC) results, allowing the identification of key stages of the curing process. The similarity between the results of both techniques is a strong indicative of the possibility of using the developed module as an alternative for industrial cure monitoring and optimization.

Surface treatments done in banana fibers (BFs) can generate significant superficial structural changes enabling the production of mechanically stronger composites. In this way, the objective of this study was to evaluate the physicochemical and mechanical properties of banana fibers of Prata specie from inner and outer leaf sheaths, when irradiated with UV light (λmax = 400 nm) during 7 (UV7) and 15 (UV15) days. Structural and microstructural characterizations for non- and irradiated fibers were performed by, FT-IR spectroscopy and Scanning Electron Microscopy (SEM), which showed the influence of UV irradiation on BFs surface and chemical structure. The Ea involved in the thermal degradation process of InNatura fiber (188.2 kJ.mol–1) was obtained using Differential Thermal Analysis (DTA/TG). The results obtained from mechanical characterization showed that the UV7 fibers presented significant improvement in tensile strength (89.77 MPa) and elastic modulus (238.94 MPa) as compared to tensile strength (69.99 MPa) and elastic modulus (87.40 MPa) of InNatura fibers. Statistical analysis using two-way ANOVA has showed that there were no differences between mechanical properties of BFs from inner to outer leaf sheaths. UV radiation has proved to be a clean method for BF surface treatment, which can improve the mechanical properties of composites based on these fibers.